Sika® Permacor®-2330

2-pack AY-PUR top coat

Sika® Permacor®-2330 is a 2-pack acrylic polyurethane top coat. Suitable for use in hot and tropical climatic conditions.

  • Very high weather resistance and gloss- and colour retention
  • Applicable also at low temperatures down to 0 °C
Product Data Sheet Show all documents

Usage

Sika® Permacor®-2330 is used as mechanical resistant topcoat for atmospherically exposed steel surfaces - also for condensation - particularly for machinery, paper mills, engines, rollercoasters and commercial vehicles. In combination with 2-pack primers and intermediate coats of the SikaCor® and Sika® Permacor® range Sika® Permacor®-2330 offers a mechanical resistant coating system for long-life corrosion protection with high weather resistance up to corrosivity category C5-I respectively C5-M, ‘high’, according ISO 12944-5.  

Advantages

  • Very high weather resistance and gloss- and colour retention
  • Applicable also at low temperatures down to 0 °C

Packaging

Sika® Permacor®-2330

28.75 kg and 11.5 kg net.

Colour

RAL- and NCS-colour shades, glossy
Others upon request.

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

  • Approved according to German standard ‘TL/TP-KOR-Stahlbauten’, page 87 and page 97.
  • Tested according to NORSOK Standard M-501, rev. 6, system no. 1.
Product Information

Shelf life

2 years

Storage conditions

In originally sealed containers in a cool and dry environment.

Density

~1.3 kg/l

Solid content

~56 % by volume
~69 % by weight

 
Technical Information

Chemical Resistance

Weathering, water, sewage, seawater, smoke, de-icing salts, acid and lye vapours, oils, grease and short term exposure to fuels and solvents.

Temperature Resistance

Dry heat up to approximately +120 °C, short term up to +150 °C
Damp heat up to approximately +50 °C

Application

Application Information

Mixing Ratio

Components A : B

By weight

100 : 15

By volume

5.1 : 1

Thinner

Sika® Thinner P

If necessary maximum 5 % Sika® Thinner P may be added to adapt the viscosity.

Product Temperature

Min. +5 °C

Relative Air Humidity

Maximum 85 %, except the surface temperature is significantly higher than the dew point temperature, it shall be at least 3 K above dew point.
The surface must be dry and free from ice.

Surface Temperature

Min. 0 °C / Max. 40 °C

Pot Life

At +10 °C

~8 h

At +20 °C

~6 h

At +30 °C

~3 h

Drying Stage 6

Drying stage 6 and waiting time between coats:

Dry film thickness 80 μm

0 °C after

48 h
+5 °C after

24 h

+10 °C after18 h
+15 °C after10 h
+20 °C after8 h
+25 °C after6 h
+30 °C after4 h

Drying time

Final drying time

The full hardness is achieved within approximately 7 days at +20 °C. Tests of the completed coating system should only be carried out after final curing.
Consumption

Consumption

Theoretical material-consumption/VOC without loss for medium dry film thickness:

Dry film thickness

50 μm

80 μm

Wet film thickness

90 μm

145 μm

Consumption

~0.115 kg/m2

~0.185 kg/m2

VOC~36.0 g/m2~57.6 g/m2

These figures are theoretical and do not allow for any additional material due to surface colour, surface porosity and surface profile variations in level and wastage etc.
Application steps

SURFACE PREPARATION

Steel:

Blast cleaning to Sa 2 ½ according to ISO 12944, part 4.

Free from dirt, oil and grease.


Hot dip galvanized steel, stainless steel and aluminium:

Free from dirt, oil, grease and corrosion products.

In case of exposure to permanent condensation the surfaces must be slightly sweep blasted with a ferrite-free blasting abrasive.


For contaminated surfaces for example galvanized or primed areas we recommend to clean with SikaCor® Wash.

MIXING

Stir component A very thoroughly using an electric mixer (start slowly, then increase up to approximately 300 rpm). Add component B carefully and mix both components very thoroughly (including sides and bottom of the container). Mix for at least 3 minutes until a homogeneous mixture is achieved. Fill mixed material into clean container and mix again shortly as described above. During mixing and handling of the materials always wear protective goggles, suitable gloves and other protective clothings.

APPLICATION

The method of application has a major effect on achieving uniform thickness and appearance. Spray application will give the best results. The indicated dry film thickness is easily achieved by airless spray. Adding solvents reduces the sag resistance and the dry film thickness. In case of application by roller or brush, additional applications may become necessary to achieve the required coating thickness, depending on type of construction, site conditions, colour shade etc. Prior to major coating operations a test application on site may be useful to ensure the selected application method will provide the requested results.

By brush or roller

Airless-Spraying:

  • Pressure minimum 150 bar
  • Nozzle size 0.38 - 0.53 mm (0.015 - 0.021 inch)
  • Spraying angle 40° - 80°

CLEANING OF EQUIPMENT

Sika® Thinner P