Product Data Sheet Show all documents

Sika® Ucrete® TCCS

Heavy-duty, colour-stable, encapsulation resin for enhanced aesthetics

Sika® Ucrete® TCCS is a three-part, heavy-duty, fast-cure encapsulation resin. It provides a highly aesthetic, colour-stable, matt sheen finish for the Sika® Ucrete® CS range of flooring systems.

  • Very good resistance to staining from a specific range of chemicals and food industry products
  • Very good resistance to UV exposure
  • Good yellowing resistance provides long-term colour stability
  • Fast curing
  • Non-tainting after curing
  • Good temperature resistance
Inquire Now
Product Data Sheet Show all documents

Usage

Sika® Ucrete® TCCS is used as a top coat for Sika® Ucrete® flooring systems. Please note:
  • The Product may only be used by experienced professionals.
 

Advantages

  • Very good resistance to staining from a specific range of chemicals and food industry products
  • Very good resistance to UV exposure
  • Good yellowing resistance provides long-term colour stability
  • Fast curing
  • Non-tainting after curing
  • Good temperature resistance

Packaging

7.35 kg

Refer to the current price list for available packaging variations.

Colour

Cured colour

Grey, Light Grey, Cream, Yellow, Bright Yellow, Green, Light Green, Green/ Brown, Red, Orange, Blue, Light Blue.

Product Details

Sustainability / Certifications / Approvals

CERTIFICATES AND TEST REPORTS

  • Halal Certification Europe (HCE), Sika® Ucrete®, WHFC, Certificate No. 21453-2/1/1/Y1

  • Food and Beverage Facilities Suitability, Sika® Ucrete®, HACCP, Test Report No. I-PE-769-SA-2-RG-06b

  • Indoor Air Comfort Gold EN 16516, Sika® Ucrete®, eurofins, Certificate No. IACG-321-01-01-2023
Product Information

Composition

Acrylic

Shelf life

Always refer to the best-before date of the individual packaging.

Storage conditions

The Product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to the packaging.

 
Technical Information

Tensile adhesion strength

> 2.0 N/mm² (concrete failure)

(EN 1542)

Chemical resistance

Laboratory-defined resistance to many individual chemicals. Before proceeding, contact Sika Technical Service for specific information.

Application

Application Information

Material temperature

Maximum

+22 °C

Minimum

+12 °C

Ambient air temperature

Maximum

+22 °C

Minimum

+12 °C

Dew point

Beware of condensation. The substrate and uncured applied product must be at least +3 °C above the dew point to reduce the risk of condensation or blooming on the surface of the applied product. Low temperatures and high humidity conditions increase the probability of blooming.

Substrate temperature

Maximum

+22 °C

Minimum

+10 °C

Curing time

The floor can be returned to service after 2 hours.

Note: Times are approximate and will be affected by changing ambient and substrate conditions.

Waiting time to overcoating

Minimum

2–3 hours

Maximum

48 hours

Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.
Consumption

Consumption

System

Consumption

Area

Sika® Ucrete® CS10

0.4–0.6 kg/m2

12–18 m2 per unit

Sika® Ucrete® CS10 AS

0.4–0.6 kg/m2

12–18 m2 per unit

Sika® Ucrete® CS20

Slip resistance R13

0.7–0.9 kg/m2

8–10 m2 per unit

Sika® Ucrete® CS20

Slip resistance R12

1.0–1.2 kg/m2

6–7 m2 per unit

Sika® Ucrete® CS20 AS

0.7–0.9 kg/m2

8–10 m2 per unit

Sika® Ucrete® CS30

1.0–1.2 kg/m2

6–7 m2 per unit

Note: Consumption data is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply the Product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.
Application steps

APPLICATION

Application must be undertaken by a fully trained and licensed Sika® Ucrete® applicator, as per recommendations stated in Sika® Ucrete® Application Manual (refer to related system application).