SikaWrap®-600 C WV

Woven unidirectional carbon fibre fabric, designed for structural strengthening applications as part of the Sika® strengthening system

SikaWrap®-600 C WV is a unidirectional woven heavy carbon fibre fabric with mid-range strength, designed for installation using the wet application process. Suitable for use in hot and tropical climatic conditions.

  • Multifunctional fabric for use in many different strengthening applications
  • Flexible and accommodating of different surface planes and geometry (beams, columns, chimneys, piles, walls, soffits, silos etc.)
  • Low density for minimal additional weight
  • Extremely cost effective in comparison to traditional strengthening technique
Inquire Now

Contact us if document is not available

Show all documents

Usage

Structural strengthening of reinforced concrete, masonry, brickwork and timber elements or structures, to increase flexural and shear loading capacity for:
  • Improved seismic performance of masonry walls
  • Replacing missing steel reinforcement
  • Increasing the strength and ductility of columns
  • Increasing the loading capacity of structural elements
  • Enabling changes in use / alterations and refurbishment
  • Correcting structural design and / or construction defects
  • Increasing resistance to seismic movement
  • Improving service life and durability
  • Structural upgrading to comply with current standards
   

Advantages

  • Multifunctional fabric for use in many different strengthening applications
  • Flexible and accommodating of different surface planes and geometry (beams, columns, chimneys, piles, walls, soffits, silos etc.)
  • Low density for minimal additional weight
  • Extremely cost effective in comparison to traditional strengthening technique

Packaging

Fabric length per roll

Fabric width

1 roll in a carboard box

≥ 50 m

500 mm

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

  • USA: ACI 440.2R-08, Guide for the Design and construction of Externally Bonded FRP Systems for strengthening concrete structures, July 2008
  • UK: Concrete Society Technical Report No. 55, Design guidance for strengthening concrete structures using fibre composite material, 2012.
Product Information

Construction

Fibre orientation

0° (unidirectional)

Warp

Black carbon fibres 95 %

Weft

E-Glass 5 %

Fibre Type

Selected mid-range strength carbon fibres

Shelf life

24 months from date of production

Storage conditions

Store in undamaged, original sealed packaging, in dry conditions at temperatures between +5 °C and +35 °C.
Protect from direct sunlight, heat and moisture.

Dry Fibre Density

1.81 g/cm3

Dry Fibre Thickness

0.331 mm (based on fibre content)

Area Density

600 g/m2 ± 20 g/m2 (carbon fibres only)

Dry Fibre Tensile Strength

4 000 N/mm2(ISO 10618)

Dry Fibre Modulus of Elasticity in Tension

230 000 N/mm2(ISO 10618)

Dry Fibre Elongation at Break

2.1 %(ISO 10618)
System information

System Structure

The system build-up and configuration as described must be fully complied with and may not be changed.

Concrete substrate adhesive primer

Sikadur®-330 or

Sikadur®-300

Impregnating / laminating resin

Sikadur®-300

Structural strengthening fabric

SikaWrap®-600 C WV


For detailed information on Sikadur®-330 or Sikadur®-300, together with the resin and fabric application details, please refer to the Sikadur®-330 or Sikadur®-300 Product Data Sheet and to the relevant Method Statement.

 
Technical Information

Laminate Nominal Thickness

0.331 mm

Laminate Nominal Cross Section

331 mm2 per m width

Laminate Tensile Strength

AverageCharacteristic
3 500 N/mm23 200 N/mm2

Laminate Modulus of Elasticity in Tension

Average

Characteristic

235 kN/mm2200 kN/mm2

* modification: sample with 50 mm
Values in the longitudinal direction of the fibres
Single layer, minimum 27 samples per test series

Laminate Elongation at Break in Tension

1.56 %

1.59 %

(based on EN 2561)

(based on ASTM 3039)

Tensile Resistance

Average

Characteristic

1155 N/mm

1056 N/mm

Tensile Stiffness

Average

Characteristic

74.3 MN/m

72.6 MN/m

74.3 kN/m per ‰ elongation

72.6 kN/m per ‰ elongation

Average

Characteristic

72.6 MN/m

69.3 MN/m

72.6 kN/m per ‰ elongation

69.3 kN/m per ‰ elongation

Application

Consumption

Consumption

Wet application with Sikadur®-300

First layer including primer

0.8–1.2 kg/m2

Following layers

0.85–1.0 kg/m2

Application with Sikadur®-330 as primer and Sikadur®-300

Primer layer

0.4–0.6 kg/m2

Fabric layers

0.85–1.0 kg/m2

 

Application steps

SUBSTRATE QUALITY

Minimum substrate tensile strength: 1.0 N/mm2 or as specified in the strengthening design.
Please also refer to the relevant Method Statement for further information.

SUBSTRATE PREPARATION

Concrete must be cleaned and prepared to achieve a laitance and contaminant free, open textured surface.
Please also refer to the relevant Method Statement for further information.