SikaCeram®-502 TG AE

SikaCeram®-502 TG AE complies to requirements of EN 13888 for class CG2 A and follows the main requirements of ANSI 118.6 for standard unsanded cement grout and compressive strength for ANSI 118.7.

Cement, polymers, fillers and additives.

Plastic bag - 24 months from date of production.

Paper bag - 12 months from date of production.

Store in cool and dry conditions in unopened, undamaged and sealed original packaging at temperatures between +10 °C and +40 °C. Protect from direct sunlight, heat and moisture.

0.150 mm

Cold, clean water by weight of powder:

1.5 L per 5 kg bag and 6.0 L per 20 kg bag (grey, white and off-white)

1.4 - 1.5 L per 5 kg bag and 5.6 - 6.0 L per 20 kg bag (other coulours)

~1.60 kg/l (grey, white and off-white)

~1.80 kg/l (other colours)

+5 °C min. / +40 °C max.

+5 °C min. / +40 °C max.

~45 min (grey, white and off white at +25 °C)

~30 min (other coulours at +25 °C)

(+25 °C)

Consumption of SikaCeram®-502 TG AE is dependent on the surface profile and roughness of the substrate as well as on the size of the tiles and the joints between them.
As a general guide, the approximate consumption can be calculated by volume, where ~1,6 - 1,8 kg/m²/mm of material is required, depending from colour.

Consumption of tile grout can be also calculated through the following formula:
((L1+ L2) x W x T x D ) / (L1 x L2) , where:
▪ L1 = Length of tile (mm) - First side
▪ L2 = Length of tile (mm) - Second side
▪ W = Joint width (mm)
▪ T = Tile thickness (mm)
▪ D = Fresh mortar density of tile grout (kg/l)
Note: Final result will be in kg/m2 .
Note: All figures are theoretical and for indicative purpose only. They do not allow for any additional material due to surface porosity, surface profile, variations in level and wastage, etc.

• Pour the recommended amount of water into a suitable, clean mixing container. Stir slowly, whilst slowly adding the SikaCeram®-502 TG AE powder to the water and then mix thoroughly using a low speed (<500 rpm.) drill mixer until the material is fully homogeneous and lump free.
• After mixing, leave the product to stand and ‘mature’ for a few minutes, then briefly stir again prior to application. The finished mix has a very creamy consistency, is uniformly coloured and it is easy to apply and spread.
• For areas requiring only small quantities, these can be mixed by hand, however please measure the water : powder ratio carefully, as even small differences in the mix ratio between batches can result in colour shade variations.
• Premature exposure to water or excess water in the mix can result in white efflorescence on the grout surface.
• In case of high-performances demanding applications, such as heavy-traffic floors, replacement of mixing water with SikaLatex® or SikaBond® DV is suggestible.

• SikaCeram®-502 TG AE is applied using a rubber blade or trowel using cross-hatch techniques, taking care to ensure the joints are filled uniformly across the whole width and along their full length.
• Using the same blade/trowel in a vertical position, remove the excess from the surface of the tiles.
• When the material starts to set, it is possible to begin the initial cleaning step, using a damp sponge. The remaining grout traces on the tile surfaces can easily be removed the next day by wiping with a clean, soft dry cloth. When SikaLatex® or SikaBond DV® has been used instead of water in the mix, this additional step should be done immediately after the initial cleaning with a damp sponge.
• Avoid application in direct sunlight and/or in excessive draughts or strong winds.

Clean all tools and application equipment with clean water immediately after use. Hardened / cured material can only be mechanically removed.