SikaCeram®-118
HIGH PERFORMANCE, LATEX CONTAINING, WATER RESISTANT, CEMENTITIOUS TILE ADHESIVE FOR THIN BED APPLICATION
SikaCeram®-118 is a high performance, C1 TE class, one-pack, polymer - latex containing, water resistant, premixed adhesive.
Consisting of high resistance cements, selected silicon / quartz mineral charges and specific additives, used as thin bed tile adhesive for permanent fixing of ceramic tiles.
Suitable for use in hot and tropical climatic conditions.
- Very good adhesion
- Easy to mix and use
- Excellent workability and thixotropic consistency
- Water and weather resistant
- Single component system
Usage
- Suitable for bonding of high absorption ceramic tiles, erthenware, extruded and refined porcelain tiles (only indoor)
- Industial enviroment, wet areas (bathrooms, kitchens, balconies, terraces, etc.)
- Suitable for indoor floor and wall applications, as well as external floor applications.
- Suitable for moisture tolerant natural stone
- Suitable for application above concrete, mortar, bricks and plaster
Advantages
- Very good adhesion
- Easy to mix and use
- Excellent workability and thixotropic consistency
- Water and weather resistant
- Single component system
Packaging
25 kg and 40 kg bag
Colour
Grey or white powder
Product Details
SUSTAINABILITY
- SikaCeram®-118 is certified according "Low Emitting Materials as per Al Sa'fat - Dubai Green Building Evaluation System" by Dubai Central Laboratory (DCL), certificate No. CL17020432
- California Department of Public Health (CDPH) Method - VOC emission test: PASS
APPROVALS / CERTIFICATES
SikaCeram®-118 follows the main requirements of EN 12004 class C1 TE and ANSI 118.4 for shear strength.
Composition
Portland cement, selected aggregates and latex polymers
Shelf life
12 months minimum from date of production
Storage conditions
Store in undamaged, unopened, original sealed packaging in dry conditions at temperatures between 5 °C and 35 °C. Protect from direct sunlight, heat and moisture.
Maximum grain size
~0.5 mm
Volatile organic compound (VOC) content
<1 g/l | (US EPA 24) |
System structure
In normal conditions on cement based substrate, no primer is required.
However, for very high absorbent substrates (e.g. drywalls) or non-absorbent substrates, please contact Sika Technical Department for recommendation.
Tensile adhesion strength
grey w/p = 0.22 white w/p = 0.23 | Value | Requirements EN 12004-1, class C1 |
Initial | ≥ 0.7 N/mm2 | ≥ 0.5 N/mm2 |
After water immersion | ≥ 0.5 N/mm2 | ≥ 0.5 N/mm2 |
After heat ageing | ≥ 0.5 N/mm2 | ≥ 0.5 N/mm2 |
Application
Slip resistance
Value w/p=0.22 | Requirements EN 12004-1, class T |
≤ 0.5 mm | ≤ 0.5 mm |
Mixing ratio
5.5 to 5.75 L of water per 25 kg bag, 8.8 to 9.2 L of water per 40 kg bag
Layer thickness
Min. 2 mm
Max. 5 mm (locally up to 12 mm thickness possible, for leveling purpose)
Ambient air temperature
+5 °C min. / +35 °C max.
Substrate temperature
+5 °C min. / +35 °C max.
Pot Life
~5 h (23 °C)
Open Time
~20 min. (23 °C) | (EN 12004-2) |
Adjustability time
~40 min. (23 °C)
Applied product ready for use
Floor tiles can be grouted | After 24 - 36 h |
Wall tiles can be grouted | After 4 - 6 h |
Surface can be used after | After 14 d |
Values determined in laboratory conditions: +23 °C ± 2 °C, R.H. 50 % ± 5 %.
Higher temperatures will reduce the indicated waiting times, lower temperatures increase waiting time.
Consumption
Powder consumption and coverage depends on the surface profile and roughness of the substrate, size and reverse profile of the tiles and the placing technique (simple placing "floating" or back to back “buttering-floating”).
As a guide:
For 1 mm thickness over 1 m2 area approximately 1.4 kg of powder is required.
For small sized tiles (side ≤30 cm), use small squared notch size trowel (4-6 mm) and progressively increas for medium tiles (side ≤45 cm, trowel 6-8mm) or large tiles (side ≤60 cm, trowel 8-10 mm)
This figure is theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.
EQUIPMENT
Select the most appropriate equipment required for the project:
Substrate preparation equipment
- Grinding equipment
- Abrading equipment
- Power washing equipment
- Sandblasting equipment
Mixing equipment
- Low speed electric single or double paddle mixer (300–400 rpm) with a spiral mixing paddle.
Application equipment
- Notched trowel
MIXING
- Mix a bag with the necessary, above mentioned, amount of water, using an electric blender with a suitable mixing spiral at low speed, in a clean bucket, and up to obtain a smooth paste free of lumps.
- Use a blender at 500 rpm maximum; do not mix at faster rate because of mechanical strength decay of the cured product.
- After blending, leave the product curing for 5 minutes in the mixing container and then briefly stir the mix prior to application.
- Always start with minimum recommended quantity of water (water/powder ratio), only if required, gradually add water to desired consistency. Do not exceed maximum allowed limit of water per bag weight.
- The obtained mix results should be very creamy, easily spreadable and thixotropic.
- Do not mix more material than can be used within 60 minutes.
APPLICATION
SikaCeram®-118 is applied using notched trowel.
The amount of product should be enough to ensure complete wetting of the tiles rear. Tiling has to be carried out on fresh glue, exerting an adequate pressure to ensure contact with the adhesive, and thus the perfect bonding. In case a surface film is formed on the adhesive, it is necessary to wipe the trowel on the adhesive layer previously applied. Avoid wetting already applied adhesive with water, as it may negatively affect its properties.
Note: For tiles > 900 cm2 (30 x 30 cm), the double spreading ("buttering") technique is always recommended.
Adhesive application
- Apply sufficient adhesive to the prepared fixing surfaces with the notched trowel to the required bed thickness.
- Adjust tiles if required.
- Clean off surplus adhesive from tile face and between tile joints before the adhesive has dried.
CLEANING OF EQUIPMENT
Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be removed mechanically.