Product Data Sheet Show all documents

SikaCeram®-200 BH

Formerly known as SikaCeram®-200                                                                                                         HIGH PERFORMANCE, POLYMER CONTAINING, WATER RESISTANT CEMENTITIOUS TILE ADHESIVE

SikaCeram®-200 BH is a high performance, one-pack, polymer containing, water resistant, premixed adhesive. Consisting of high resistance cements, selected silicon / quartz mineral charges and specific additives, used as thin bed tile adhesive for permanent fixing of ceramic tiles. Suitable for use in hot and tropical climatic conditions.

  • Very good adhesion
  • Easy to mix and use
  • Excellent workability and thixotropic consistency
  • Water resistant
  • Extended open time
  • Single component system
Product Data Sheet Show all documents

Usage

  • Suitable for bonding of highly absorbent ceramic tiles, earthenware, extruded and refined porcelain tiles.
  • Suitable for bonding of large size tiles used in industrial environment, wet areas, pool sides.
  • Suitable for bathrooms, kitchens, balconies, terraces, swimming pools etc.
  • Indoor and outdoor application over concrete, cement mortars, bricks and plaster.
  • Suitable for moisture tolerant natural stone
  • Suitable to tile directly on various Sika waterproofing products
 

Advantages

  • Very good adhesion
  • Easy to mix and use
  • Excellent workability and thixotropic consistency
  • Water resistant
  • Extended open time
  • Single component system

Packaging

20 kg bag

Colour

Grey and white powder

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

SikaCeram®-200 BH follows the main requirements of EN 12004 class C2 TE.
Product Information

Composition

Portland cement, selected aggregates and polymers

Shelf life

12 months minimum from date of production

Storage conditions

Store in undamaged, unopened, original sealed packaging in dry conditions at temperatures between +5 °C and +35 °C. Protect from direct sunlight, heat and moisture.

Maximum grain size

~0.5 mm
System information

System structure

In normal conditions no primer is required.

However for uncommon substrates please refer to Sika Technical Department.
Technical Information

Tensile adhesion strength

w/p = 0.20

Value

Requirement EN 12004, class C2

Initial

≥ 1.15 N/mm2

≥ 1.0 N/mm2

After water immersion

≥ 1.10 N/mm2

≥ 1.0 N/mm2

After heat ageing≥  1.10 N/mm2≥  1.0 N/mm2

Application

Application Information

Slip resistance

Value

Requirements

w/p=0.20

EN 12004, class T

≤ 0.5mm

≤ 0.5mm

Mixing ratio

4.0–4.2 L of water per 20 kg bag

Fresh mortar density

~1.70 kg/l (25 °C)

Layer thickness

Min. 2mm

Max. 5 mm (locally up to 12 mm thickness possible, for leveling purpose)

Ambient air temperature

+5 °C min. / +35 °C max.

Substrate temperature

+5 °C min. / +35 °C max.

Pot Life

~1.5 h (23 °C)

Open Time

≥ 20 min (23 °C)

(EN 1346)

Applied product ready for use

Floor tiles can be grouted

After 24–36 h

Wall tiles can be grouted

After 4–6 h

Full traffic / use

After 14 d
Consumption

Consumption

The consumption depends on the surface profile and roughness of the substrate and on the size of the tiles and the placing technique (simple placing "floating" or back to back "buttering-floating").

As a guide:

For 1 mm thickness over 1 m2 area approximately 1.7 kg of material.

One 20 kg bag will cover approximately ~4.7–7.1 m2 at 3–2 mm thickness.
Application steps

MIXING

Mix 20 kg bag with the necessary, above mentioned, amount of water, using an electric blender with a suitable mixing spiral at low speed, in a clean bucket, and up to obtain a smooth paste free of lumps.

Use a blender at 500 rpm maximum; do not mix at faster rate because of mechanical strength decay of the cured product.

After blending, leave the product to stand and 'mature' for 5 minutes in the mixing container and then briefly stir the mix prior to application. The obtained mix results very creamy, easily spreadable and thixotropic.

APPLICATION

SikaCeram®-200 BH is applied using notched trowel. The amount of product should be enough to ensure complete wetting of the tiles’ rear. Tiling has to be carried out on fresh glue, exerting an adequate pressure to ensure contact with the adhesive, and thus the perfect bonding. In case a surface film is formed on the adhesive, it is necessary to wipe the trowel on the adhesive layer previously applied. Avoid wetting with water of the already applied adhesive, it damages the adhesive.

CLEANING OF EQUIPMENT

Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be mechanically removed.