SikaPlast®-3600 LH

HIGH PERFORMANCE WATER REDUCING AND RETARDING CONCRETE ADMIXTURE

SikaPlast®-3600 LH is a third generation polycarboxylate based superplasticizer for concrete. It has been developed for use in ready mixed concrete giving extended slump retention and high strength development for normal grade concrete mixes.
SikaPlast®-3600 LH is suitable for use in concrete mixes containing microsilica and other pozzolanic materials like GGBS and fly ash. Suitable for use in hot and tropical climatic conditions.

SikaPlast®-3600 LH acts by surface absorption on the cement particles producing steric hindrance as well as electrostatic repulsion between cement particles which results in higher dispersion, flow and retention. SikaPlast®-3600 LH provides the following beneficial properties:
  • Substantial improvement in workability without increased water
  • Low risk of segregation
  • Normal set without retardation (within the dosage limit)
  • Improved density and surface finish
  • Improved water tightness
  • Excellent solution for continuous concrete casting of deep elements
  • Does not contain chlorides or other steel corrosion promoting ingredients therefore may be used for reinforced and pre-stressed concrete construction
Inquire Now

Contact us if document is not available

Show all documents

Usage

SikaPlast®-3600 LH facilitates high water reduction, excellent flowability with optimum cohesion and impressive slump retention characteristics.
SikaPlast®-3600 LH is used for the following types of concrete:
  • Foundations
  • Walls
  • Columns and piers
  • Piles
  • Slabs
  • Pre-stressed concrete
  • Bridges and cantilever structures
 

Advantages

SikaPlast®-3600 LH acts by surface absorption on the cement particles producing steric hindrance as well as electrostatic repulsion between cement particles which results in higher dispersion, flow and retention. SikaPlast®-3600 LH provides the following beneficial properties:
  • Substantial improvement in workability without increased water
  • Low risk of segregation
  • Normal set without retardation (within the dosage limit)
  • Improved density and surface finish
  • Improved water tightness
  • Excellent solution for continuous concrete casting of deep elements
  • Does not contain chlorides or other steel corrosion promoting ingredients therefore may be used for reinforced and pre-stressed concrete construction

Packaging

1000 L flowbin
Bulk delivery in tanker trucks is possible on request.

Colour

Light brown to brown liquid

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

SikaPlast®-3600 LH follows the requirements of ASTM C494; Type G and EN 934-2
Product Information

Composition

Aqueous solution of modified polycarboxylates and copolymers

Shelf life

12 months from date of production if stored properly

Storage conditions

Store in undamaged, unopened, original sealed packaging in dry conditions at temperatures between +5°C and +45°C. Protect from direct sunlight and frost

Density

~1.07 kg/l

Total chloride ion content

Nil

(EN 934-2)
Technical Information

Concreting guidance

The standard rules of good concreting practice for production and placing must be observed when using SikaPlast®-3600 LH in concrete. Refer to relevant standards.
Fresh concrete must be cured properly especially at high temperatures in order to prevent plastic and drying shrinkage. Use Sika® Antisol® products as a curing agent or apply wet hessian.

Application

Application Information

Compatibility

SikaPlast®-3600 LH may be combined with all types of Portland cement and the following Sika products:
▪ SikaPump®
▪ Sika® FerroGard®-901
▪ SikaFume®
▪ Sika-Aer®
▪ Sika® Control-40 (stabilizer)
▪ Sika®-WT 1
We recommend to perform trial mixes to establish the required performance when combined with the above products. Please consult our Sika Technical Department.

Dispensing

SikaPlast®-3600 LH is added to the gauging water or simultaneously poured with it into the concrete mixer at the batching plant.
Do not add SikaPlast®-3600 LH directly to the dry mix.
For optimum utilization of its high water reduction property we recommend thorough mixing at a minimal wet mixing time of 60 seconds. The addition of the remaining gauging water (to fine tune concrete consistency) may only be started after two-thirds of the wet mixing time to avoid surplus water in the concrete.

Restrictions

When using SikaPlast®-3600 LH a mix design must be selected for the local material sources used and trial mixes performed to verify suitability.
If frozen and/or if precipitation has occurred, it may only be used after thawing slowly at room temperature and intensive mixing.
SikaPlast®-3600 LH should not be added to dry cement. Before pouring, suitability tests on the fresh concrete must be carried out. Due to the extended workability take special care that formwork is properly installed and secured. In case the setting time of concrete is extended, if cured properly, other properties may not be affected and higher ultimate strength is visualized. SikaPlast® products are not compatible with admixtures based on sulfonated napthalene or melamine.
Consumption

Recommended dosage

0.8 - 2.0 % by weight of binder
Higher dosages up to 2.0 % by weight of binder can be used depending on the mix design, raw materials, climatic conditions and concrete requirements. Trial mixes must be performed to establish the exact dosage rate required.