Sika® Plastiment® PZ 392

(former MPozzolith 392)

HIGH PERFORMANCE RETARDING PLASTICISER FOR CONCRETE

Sika® Plastiment® PZ 392 is a high-performance plasticising retarder, beneficial in maintaining workability especially in high ambient temperatures. Suitable for use in hot and tropical climatic conditions.

  • Reduces placing problems in hot weather by improved workability and workability retention in conjunction with extended setting times.
  • Improves surface finish.
  • Improves trowellability.
  • Reduces honeycombing / cold joint effects.
  • Considerably improves the cohesion of concrete, reducing segregation and bleed water.
  • Improves pumpability of concrete.
  • Reduces effects of various modes of attack on concrete and embedded steel by considerable reduction in permeability.
Inquire Now

Contact us if document is not available

Show all documents

Usage

  • Ready mixed concrete where high workability retention and retardation are highly required.
  • Hot weather concreting of all types.
  • Reduction in permeability, reducing effect of groundwater salts on concrete and steel.
  • To improve cohesion, workability and compact ability in concretes using poorly graded/shaped fine aggregates.
 

Advantages

  • Reduces placing problems in hot weather by improved workability and workability retention in conjunction with extended setting times.
  • Improves surface finish.
  • Improves trowellability.
  • Reduces honeycombing / cold joint effects.
  • Considerably improves the cohesion of concrete, reducing segregation and bleed water.
  • Improves pumpability of concrete.
  • Reduces effects of various modes of attack on concrete and embedded steel by considerable reduction in permeability.

Packaging

210 L drums, 1000 L flowbin or bulk supply in tanker

Colour

Dark brown liquid

Product Details

Sustainability / Certifications / Approvals

CERTIFICATES AND TEST REPORTS

Sika® Plastiment® PZ 392 follows the requirements of ASTM C494; Types B and D and BS EN 934-2
Product Information

Composition

Modified organic compounds

Shelf life

12 months from date of production if stored properly

Storage conditions

Store in undamaged, unopened, original sealed packaging in dry conditions at temperatures between +5°C and +45°C. Mix well before use.

Density

~1.07 kg/l (+25°C)

pH-Value

5 – 8

Total chloride ion content

Nil

(BS EN 934-2)

 
Technical Information

Concreting guidance

The standard rules of good concreting practice for production and placing must be observed when using Sika® Plastiment® PZ 392 in concrete. Refer to relevant standards. Fresh concrete must be cured properly especially at high temperatures in order to prevent plastic and drying shrinkage. Use Sika® Antisol® products as a curing agent or apply wet hessian.

Application

Application Information

Compatibility

Sika® Plastiment® PZ 392 is suitable for mixes containing all types of cement and supplementary cementitious materials such as: Microsilica (Silica Fume), Fly Ash (PFA), GGBS (Ground Granulated Blast Furnace Slag) and the following Sika products:

  • Sikament® 
  • SikaPump®
  • Sika® FerroGard®
  • SikaFume®
  • SikaFiber®
  • Sika® Aer
  • Sika® Stabilizer
  • SikaControl®

We recommend to perform trial mixes to establish the required performance when combining Sika® Plastiment® PZ 392 with the above products or other admixtures. Please consult our Sika Technical Department for further assistance.

Dispensing

Sika® Plastiment® PZ 392 is added to the gauging water or simultaneously poured with it into the concrete mixer at the batching plant. Do not add Sika® Plastiment® PZ 392 directly to the dry mix. The addition of the remaining gauging water (to fine tune concrete consistency) may only be started after two-thirds of the wet mixing time to avoid surplus water in the concrete.
Consumption

Recommended dosage

Trials should be conducted to determine the optimum addition rates of Sika® Plastiment® PZ 392, depending on mix design proposed and mix performance requirements. As a general guide, a dosage range of 200 ml to 600 ml per 100 kg of total binder is recommended as a starting point. Depending on the desired properties, a dosage of up to 800 ml per 100 kg of total binder shall be used.