SikaGrout®-114 AE

CEMENTITIOUS, SHRINKAGE COMPENSATED, GENERAL PURPOSE GROUT

SikaGrout®-114 AE is a cementitious, free flowing, general purpose, non-shrink precision grout with high ultimate strength.
Suitable for use in hot and tropical climatic conditions.

SikaGrout®-114 AE is an economical and easy to use grout requiring only the addition of water. It offers the following beneficial properties:
  • Easy to mix
  • Good flow characteristics
  • Dual expansion system
  • Adjustable consistency
  • High final strengths
  • Non-corrosive and iron-free
Inquire Now

Contact us if document is not available

Show all documents

Usage

SikaGrout®-114 AE is used for grouting in the following:
  • Machine foundations
  • Columns in pre-cast construction
  • Concrete anchors, cavities, gaps and recesses
  • Base plates
  • General concrete repairs
  • Bridge bearings pads
 

Advantages

SikaGrout®-114 AE is an economical and easy to use grout requiring only the addition of water. It offers the following beneficial properties:
  • Easy to mix
  • Good flow characteristics
  • Dual expansion system
  • Adjustable consistency
  • High final strengths
  • Non-corrosive and iron-free

Packaging

25 kg bag

40 kg bag

Colour

Grey Powder

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

SikaGrout®-114 AE complies with nonshrink hydraulic cement grout requirements according ASTM C1107.
Product Information

Composition

Portland cement, selected fillers and aggregates, special additives.

Shelf life

12 months minimum from date of production.   

Storage conditions

Store in original unopened packaging in cool and dry condition between +5 °C and +35 °C. Protect from direct sunlight, heat and moisture.

Maximum grain size

~5 mm

 
Technical Information

Compressive strength

1 Day

3 Day

28 Days

w/p ratio = 0.12 (3.0 L water / 25 kg)

~30 N/mm2

~50 N/mm2

~75 N/mm2

w/p ratio = 0.13 (3.25 L water / 25 kg)

~28 N/mm2

~48 N/mm2

~65 N/mm2

Tensile strength in flexure

~14.0 N/mm2 (28 d) 

(ASTM C580)

Tensile strength

~5.5 N/mm2 (28 d)

(ASTM C307)

Tensile adhesion strength

≥ 1.5 N/mm2 (concrete failure)

(EN 1881)

Expansion

~0.11 % (28 d)

(ASTM C157)

Application

Application Information

Mixing ratio

Consistency

Water per 25 kg bag

Water/Powder ratio

Flowable

3.00 – 3.25 L

0.12 – 0.13

Highly flowable (max. flow)3.25 – 3.50 L0.13 – 0.14

Fresh mortar density

~2.20 kg/l (+25 °C)

Layer thickness

Min. 10 mm per layer

Max. 100 mm per layer

Ambient air temperature

+5 °C min. / +35 °C max.

Substrate temperature

+5 °C min. / +35 °C max.

Pot Life

~2 h (+23 °C)
Consumption

Yield

~12.8 L / 25 kg bag
Application steps

MIXING

Add water according to the desired consistency into a clean mixing vessel before slowly adding the SikaGrout®-114 AE powder. SikaGrout®-114 AE is best mixed in a forced action mixer, for 2 to 3 minutes or until the mix is free of lumps, not longer than 5 minutes. Slow speed drill (maximum 500 rpm) can be also used for mixing. Normal tumble type concrete mixers are not suitable. Do not add extra water or other ingredients. Mix only full bags for best results.

APPLICATION

Before pouring let the mixed grout stand for approximately 5 minutes after mixing to allow entrapped air to escape. Pour into the prepared area such that the grout has the shortest distance to travel. Ensure that air displaced by the grout is allowed to escape. When carrying out base plate grouting, ensure a sufficient head of pressure is maintained to keep the mortar flowing. All exposed areas of the mortar surface should be kept as small as possible.

 

CURING TREATMENT

Treat exposed surfaces with Antisol®-WB curing compounds or use other approved curing methods such as polyethylene sheeting or wet hessian. Do not commence fogging until final set has been reached.

CLEANING OF EQUIPMENT

Clean equipment and mixer immediately after application with water. Hardened material can only be removed mechanically.