SikaGrout®-214 AE

Cementitous, High Early Strength, Non-Shrink Precision Grout

SikaGrout®-214 AE is a cementitious, free flowing, economical, non-shrink precision grout with high early and ultimate strength.
Suitable for use in tropical and hot climatic conditions.

SikaGrout®-214 AE is an easy to use grout requiring only the addition of water. It offers the following beneficial properties:
  • Easy to mix
  • High early strength
  • Good flow characteristics
  • Dual expansion system
  • Adjustable consistency
  • High final strengths
  • Non-corrosive and iron-free
Inquire Now

Contact us if document is not available

Show all documents

Usage

SikaGrout®-214 AE precision grout is used for grouting in the following:
  • Machine Foundations
  • Columns in pre-cast construction
  • Base plates
  • Concrete anchors, cavities, gaps and recesses
  • General concrete repairs
  • Joint nosing
 

Advantages

SikaGrout®-214 AE is an easy to use grout requiring only the addition of water. It offers the following beneficial properties:
  • Easy to mix
  • High early strength
  • Good flow characteristics
  • Dual expansion system
  • Adjustable consistency
  • High final strengths
  • Non-corrosive and iron-free

Packaging

25 kg bag

Colour

Grey Powder

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

SikaGrout®-214 AE follows the main requirements of ASTM C1107 and CRD-C621-83-10.2.
Product Information

Composition

Portland cement, selected fillers and aggregates, special additives.

Shelf life

12 months minimum from date of production.

Storage conditions

Store in original unopened packaging in a cool and dry condition between +5 °C and +35 °C. Protect from direct sunlight, heat and moisture.

Maximum Grain Size

~5 mm

 
Technical Information

Compressive Strength

 (25 °C)

1 Day

28 Days

w/p = 0.12 (3.0 L water / 25 kg)~45 N/mm2~80 N/mm2
w/p = 0.13 (3.25 L water / 25 kg)~30 N/mm2~65 N/mm2

Tensile Strength in Flexure

~14.5 N/mm2 (28 d)

(BS 4551)

Tensile Strength

~5.5 N/mm2  (28 d)(ASTM C307)

Tensile Adhesion Strength

≥ 1.5 N/mm2 (or concrete failure)

(EN 1881)

Expansion

Nil (28 d)

(ASTM C940)

Water Absorption

~1.6 % (28 d)

(EN 1881)

Application

Application Information

Mixing Ratio

ConsistencyWater per 25 kg bagWater/Powder Ratio
Flowable (max. strength)3.0 - 3.25 L0.12 - 0.13
Highly Flowable (max. flow)3.25 - 3.5 L0.13 - 0.14

Fresh Mortar Density

~2.20 kg/l (+25°C)

Layer Thickness

Min. 10 mm per layer

Max. 100 mm per layer

Ambient Air Temperature

+5 °C min. / +35 °C max.

Substrate Temperature

+5 °C min. / +35 °C max.

Pot Life

~ 2 h (23 °C)
Consumption

Yield

~12.8 L / 25 kg bag
Application steps

MIXING

Add water according to the desired consistency into a clean mixing vessel before slowly adding the SikaGrout®-214 AE powder. SikaGrout®-214 AE is best mixed in a forced action mixer, for 2 to 3 minutes or until the mix is free of lumps, not longer than 5 minutes. Slow speed drill (maximum 500 rpm) can be also used for mixing. Normal tumble type concrete mixers are not suitable. Do not mix more grout than can be placed within 15 to 20 minutes. Do not add extra water or other ingredients. Mix only full bags for the best result.

 

APPLICATION

Before pouring let the mixed grout stand for approximately 5 minutes after mixing to allow entrapped air to escape. Pour into the prepared area such that the grout has the shortest distance to travel. Ensure that air displaced by the grout is allowed to escape. When carrying out the base plate grouting, ensure a sufficient head of pressure to keep the mortar flowing. All exposed areas of the mortar surface should be kept as small as possible.

CURING TREATMENT

Treat exposed surfaces with Antisol-E curing compound or use other approved curing methods such as polyethylene sheeting or wet hessian.

Do not commence fogging until final set has been reached.

CLEANING OF EQUIPMENT

Clean equipment and mixer immediately after application with water. Hardened material can only be removed mechanically.