Sikasil®-728 SL

Self-leveling, ultra-low modulus, neutral cure silicone sealant for concrete pavements

Sikasil®-728 SL is a self-leveling, 1-component, ultra-low modulus, elastomeric, neutral cure silicone sealant. Suitable for use in hot and tropical climatic conditions.

  • No tooling, less labour
  • Very high movement capability
  • Very good adhesion, especially to concrete
  • Very long service life due to outstanding UV resistance
  • Very good flexibility for use in extremely high and low temperatures
  • Resistance to jet fuel and road salts
Inquire Now

Contact us if document is not available

Show all documents

Usage

Sikasil®-728 SL is designed to seal horizontal saw cut and expansion joints in concrete pavements on highways, airports, bridges, walkways, parking garages and driveways. Suitable substrates for Sikasil®-728 SL are concrete, steel, glass, aluminium, masonry, asphalt, brick, natural stone and others. Sikasil®-728 SL can be used on slopes of up to 3 %.  

Advantages

  • No tooling, less labour
  • Very high movement capability
  • Very good adhesion, especially to concrete
  • Very long service life due to outstanding UV resistance
  • Very good flexibility for use in extremely high and low temperatures
  • Resistance to jet fuel and road salts

Packaging

858 mL cartridge, 12 cartridges per box

600 mL foil pack, 20 foil packs per box

17 L pail

197 L drum

Colour

Limestone

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

  • ASTM C920, Type S, Grade P, Class 100/50, Use T2, M, G, A, O
  • ASTM D 5893 Type SL
  • TT-S-00230C, Type I, Class A
  • TT-S-001543A, Class A
  • US Federal Specification SS-S-200E Flame Resistance (section 4.4.12)
  • FAA AC 150/5370-10G Item P-605
Product Information

Composition

Neutral cure silicone

Shelf life

Sikasil®-728 SL has a shelf life of 12 months from the date of production, if it is stored properly in undamaged, original, sealed packaging, and if the storage conditions are met.

Storage conditions

Sikasil®-728 SL shall be stored in dry conditions, where it is protected from direct sunlight and at temperatures between +5 °C and +25 °C.

Density

~1.25 kg/l

(ISO 1183-1)
Technical Information

Shore Hardness

~40 (Shore OO 21 d)(ASTM C 661, ASTM D 2240, ISO 868)

Shore A Hardness

~5 (after 21 days)

(ASTM C 661, ASTM D 2240, ISO 868)

Tensile Strength

~0.70 MPa

(ASTM D 412)

Tensile Stress at Specified Elongation

~0.18 MPa at 100 % elongation

(ASTM D 412)

~0.19 MPa at 150 % elongation

Adhesion in Peel

~4 N/mm on mortar substrate

(ASTM C 794)

Movement Capability

+100 % / -50 %

(ASTM C 719)

Chemical Resistance

Sikasil®-728 SL is resistant to water, road salts, seawater, diluted alkalis, cement slurry and water dispersed detergent.
Sikasil®-728 SL is temporarily resistant to jet fuel spillage.
Sikasil®-728 SL is not resistant to alcohols, organic acids, concentrated alkalis and acids and chlorinated hydrocarbons.

Resistance to Weathering

0 (no cracks)

(ASTM C 793)

Service Temperature

-60 °C min. / +175 °C max.

Joint Design

The spacing between joints and joint dimensions must be designed to suit the joint movement required and the movement capability of the sealant. The joint width shall be ≥ 6 mm and ≤ 25 mm. The joint depth shall between 0.5 and 0.8 of the joint width (width:depth ratio of 2 : 1 – 1 : 0.8) but always  ≥ 6 mm and ≤ 13 mm. The joint shall be recessed half of the joint width but always ≥ 10 mm. For larger joints, please contact our Technical Department.

Standard joint dimensions for joints between concrete elements

Joint width [mm]

Joint depth [mm]

Recessed below surface [mm]

6

6

10

10

6

10

15

8

10

20

10

10

25

13

13

All joints must be correctly designed and dimensioned in accordance with the relevant standards before their construction. The basis for calculation of the necessary joint widths are the type of structure and its dimensions, the properties of the adjacent building materials and the joint sealing material, as well as the specific exposure of the building and the joints.

 

Application

Application Information

Backing Material

Use closed cell, polyethylene foam backing rods 25 % larger than the joint width. If the joint depth does not allow for backer rod, use polyethylene bond breaker tape to prevent three-sided adhesion.

Sag Flow

Self-leveling, can be used on slopes ≤ 3 %

Ambient Air Temperature

+5 °C min. / +40 °C max. (min. 3 °C above dew point temperature)

Substrate Temperature

+5 °C min. / +40 °C max.
Sealants should be installed when substrates are at mid-range of their anticipated movement.

Curing Rate

~3.5 mm/d(CQP 049-2)

Skinning time

~60 min (23 °C / 50 % r.h.)

(ISO 019-1)

Tack free time

~115 min (23 °C / 50 % r.h.)

(ASTM C 679)
Application steps

SUBSTRATE PREPARATION

The substrate must be clean, dry, sound and homogeneous, free from oils, grease, dust and loose or friable particles. Paint, cement laitance and other poorly adhering contaminants must be removed. Sikasil®-728 SL adheres without primers and/or activators.
However, for optimum adhesion, long term durability and critical, high performance applications, highly stressed joints, extreme weather exposure or water immersion, the following priming and/or pre-treatment procedures shall be followed:
 

Porous substrates
Concrete shall be primed with Sika® Primer-3 N applied with a clean brush. Before sealing, allow a flash-off time of > 30 minutes (< 4 hours).

 

Non- porous substrates
On aluminium, anodised aluminium, stainless steel and galvanised steel, Sika® Aktivator-205 shall be applied using a clean towel. Before sealing allow a flash-off time of > 15 minutes (< 2 hours).

For detailed advice, please contact our Technical Department.

 

CLEANING OF EQUIPMENT

Clean all tools and application equipment immediately after use with Sika® Remover-208 and/or Sika® TopClean T. Once cured, residual material can only be removed mechanically.