Sikasil®-117 Sanitary
ACETOXY SILICONE SEALANT FOR SANITARY APPLICATIONS
Sikasil®-117 Sanitary is a 1-component, solvent-free sealant with resistance to fungus.
Suitable for use in hot an tropical climatic conditons.
- Low shrinkage
- Mildew and fungus resistant
- Good UV and weathering resistance
Usage
Sikasil®-117 Sanitary is designed for sanitary or other sealing applications in wet rooms where mildew resistance is required. Sikasil®-117 Sanitary is designed to seal glass, glazed surfaces, ceramic and porcelain and cotaed metal substrates.Advantages
- Low shrinkage
- Mildew and fungus resistant
- Good UV and weathering resistance
Packaging
280 ml cartridges, 12 cartridges per box
Colour
Clear, white, cream, brown, beige and grey (other colors on request)
Product Details
SUSTAINABILITY
Sikasil®-117 Sanitary conforms to LEED® v3 IEQ 4.1
▪ VOC content <50 g/l (US EPA method 24)
Composition
Acetoxy silicone
Shelf life
Sikasil®-117 Sanitary has a shelf life of 12 months from the date of production, if it is stored properly in undamaged, original, sealed packaging, and if the storage conditions are met.
Storage conditions
Sikasil®-117 Sanitary shall be stored in dry conditions, protected from direct sunlight and at temperatures between +5 °C and +25 °C.
Density
| ~0.98 kg/l | (ISO 1183-1) |
Volatile organic compound (VOC) content
| <50 g/l | (US EPA method 24) |
Shore A hardness
| ~20 (28 d / 23 °C / 50 % r.h.) | (ASTM D-661) |
Service temperature
-40 °C min. / +180 °C max.
Application
Sag flow
| non sag | (ASTM C-639) |
Ambient air temperature
+5 °C min. / +45 °C max.
Substrate temperature
+5 °C min. / +45 °C max.
Curing rate
| ~3 mm/24 h (23 °C / 50 % r.h.) | (CQP 049-2) |
Skinning time
| ~15 min (23 °C / 50 % r.h.) | (CQP 019-1) |
Tack free time
| ~25 min (23 °C / 50 % r.h.) | (CQP 019-1) |
SUBSTRATE PREPARATION
The substrate must be clean, dry, sound and homogeneous, free from oils, grease, dust and loose or friable particles. Paint, cement laitance and other poorly adhering contaminants must be removed. Sikasil®-117 Sanitary adheres without primers and/or activators.
However, for optimum adhesion and critical, high performance applications, such as on multi-story buildings, highly stressed joints, extreme weather exposure or water immersion, the following priming and/or pretreatment procedures shall be followed:
Aluminium, anodised aluminium, stainless steel, galvanised steel, powder coated metals or glazed tiles have to be cleaned and pre-treated using Sika® Aktivator-205, wiped on with a clean towel. Before sealing, allow a flash-off time of >15 minutes (<2 hours). Other metals, such as copper, brass and titanium-zinc, also have to be cleaned and pre-treated using Sika® Aktivator-205, wiped on with a clean towel. After the
necessary flash-off time, use a brush to apply Sika® Primer-3 N and allow a further flash-off time of >30 minutes (<4 hours) before sealing the joints. PVC has to be cleaned and pre-treated using Sika® Primer-215 applied with a brush. Before sealing, allow
a flash-off time of >30 minutes (<4 hours). Glass shall be cleaned with isopropyl alcohol before
application.
Note: Primers are adhesion promoters. They are neither a substitute for the correct cleaning of a surface, nor do they improve the strength of the surface significantly. For more detailed advice and instructions please contact our Technical Department.
CLEANING OF EQUIPMENT
Clean all tools and application equipment immediately after use with Sika® Remover-208. Once cured, residual material can only be removed mechanically.