SikaInject®-311

(former TPH. ® RUBBERTITE)

3-part rubberlike, flexible acrylate resin

3-part, acrylate-/methacrylate-based water-expanding hydrogel that hardens to a rubber-like, flexible product.

  • Extreme low viscosity
  • Very good penetration into finest aggregates
  • Rubberlike flexible product
  • Good chemical resistance (many acids, alkalis, hydrocarbons)
  • Suitable also for damp proof courses in brickwork
  • Optional polymeric strengthening with SikaInject®-315 PS
  • Optional retarder SikaInject®-311 SL for extreme long potlife
Inquire Now
Show all documents

Usage

Waterproofing of cracks, joints and honeycombs. Injection into masonry, concrete structures, civil engineering construction and tunneling. Sealing of annular gaps in tunnels and shaft applications. Repair of failed warterbars/expansion joints in combination with a polymeric strengthening (PS) compound. Curtain injection into ground and sand.  

Advantages

  • Extreme low viscosity
  • Very good penetration into finest aggregates
  • Rubberlike flexible product
  • Good chemical resistance (many acids, alkalis, hydrocarbons)
  • Suitable also for damp proof courses in brickwork
  • Optional polymeric strengthening with SikaInject®-315 PS
  • Optional retarder SikaInject®-311 SL for extreme long potlife

Packaging

part A1: 20 kg

part A2: 1 kg

part B2: 0.3 kg

optional PS compound SikaInject®-315 PS: 20 kg

Colour

part A1: transparent, liquid

part A2: colorless, liquid

part B2: white, solid

Product Details

Sustainability / Certifications / Approvals

CERTIFICATES AND TEST REPORTS

  • CE-Marked acc.to EN 1504-5 (S, swelling-fitted filling of cracks, alone and combined with the polymeric-strengthening (PS) compound SikaInject®-315 PS)
  • German General Building Inspectorate Approval as an injection product for curtain grouting
  • DIBt-certificate for use as a crack filler acc. to German Reinforced Concrete Committee (DAfStb) in combination PS.

Product Information

Shelf life

12 months from date of production in original packaging

Storage conditions

dry, between 15 °C - 25 °C, protected from heat, frost and direct sunlight

Density

part A1: ~ 1.06 kg/l (DIN EN ISO 3675)

part A2: ~ 0.93 kg/l (DIN EN ISO 3675)

part B2: ~ 2.59 kg/l

 

Viscosity

part A1: ~ 15 mPas (DIN EN ISO 2555)

part A2: ~ 8 mPas (DIN EN ISO 2555)

mix AB: ~ 3 mPas (DIN EN ISO 2555)

Consistency

Rubberlike

Technical Information

Modulus of elasticity in flexure

~0.13 MPa

(DIN EN ISO 527)

Tensile strength

~0.08 MPa

(DIN EN ISO 527)

Water absorption

~20 %

(DIN EN ISO 62)

Elongation at break

~290 %

(DIN EN ISO 527)

Application

Application Information

Substrate temperature

5 °C - 40 °C

Pot Life

~5 min

(DIN EN 14022)

Curing time

~10 min

Application steps

SUBSTRATE PREPARATION

Surfaces of cracks, joints and voids need to be clean, free of loose particles, dust, oil and any other bond-breaking substances.

Any dirt must be blown out with compressed air.

MIXING

1. For curtain injection, brickwork, horizontal barrier (dpc) and ground stabilisation:

  • Empty part A2 completely into the part A1 container and mix for 3 minutes (part A1 + part A2 = Component A)
  • Fill part B2 into an equivalent 20 L container and fill with 20 L of tap water - mix for 3 minutes (part B2 + water = Component B)
  • Components A and B prepared in this way are ready-for-use, pump with a 2-C pump in a ratio 1:1 parts by volume directly from containers
 

2. For crack injection and injection hoses

  • Empty part A2 completely into the part A1 container and mix for 3 minutes (part A1 + part A2 = Component A)
  • SikaInject®-315 PS is used instead of water in Component B
  • Make sure that component B2 (hardener salt) is completely dissolved in SikaInject®-315 PS
  • Therefore: half-fill container of part B2 with tap-water and shake until part B2 salt is completely dissolved
  • Fill this salt-solution into container of SikaInject®-315 PS and mix for 3 minutes (part B2 + water + PS = Component B)
  • Components A and B prepared in this way are ready-for-use, pump with a 2-C pump in a ratio 1:1 parts by volume directly from containers.

Activated components A and B remain stable for approx. 5 hours (depending on temperature).
 